For large gear tooth surface

And induction hardening, flame hardening, carburizing and quenching processes, laser hardening hardened layer, high hardness (typically higher than the induction hardening 1-3HRC), workpiece deformation is small, the heating depth and easy to control the heating path, easy to automate , did not like the induction hardening of parts of different sizes according to design appropriate induction coil. Gifts of  laser pointer  are good choices.
The processing of large parts need not be case hardening heat treatment furnace size and other chemical constraints, in many industries to gradually replace the CKS and the chemical induction hardening heat treatment and other traditional crafts. Of particular importance is the deformation of the workpiece before and after laser hardening is almost negligible, it is particularly suitable for high-precision surface treatment of parts required. The depth of the laser hardened layer in accordance with part composition, size and shape of the laser process parameters and different, usually in the range 0.3 ~ 2.0mm. For large gear tooth surface, large parts of the journal shaft quenching, the surface roughness is essentially the same, no subsequent machining to meet the needs of the actual working conditions. More gifts of  laser pointer  will be recommended to the customer.
Laser melting quenching technique is the use of a laser beam to the substrate surface is heated to above the melting temperature, the thermal conductivity of the substrate within the surface layer quickly cooled leaving the melting and solidification cooling crystallization process. Quenching obtained by melting a very dense, along the depth direction of the organization were melting - solidification layer, phase transformation hardening layer, heat affected zone and substrate. Laser melting layer than the depth of laser hardening hardening layer deeper, higher hardness, wear resistance and better. Inadequacies of the technology lies in the surface roughness of a certain degree of damage, generally require subsequent machining to recover. In order to reduce the laser melting treatment part surface roughness and reduce the amount of follow-up process, Huazhong University of Science and Technology prepared a special laser melting hardening coatings, can significantly reduce the melting layer of the surface roughness. The company has more options of  laser pointer  for the customer.